Shrinkage Kinetics during Sintering W-Ni-Fe Heavy Alloy with Ultrafine Grain
スポンサーリンク
概要
- 論文の詳細を見る
The characteristics of shrinkage kinetics curve of compacts of W-(Ni-Fe)10% with particle size less than 200 nm sintered in hydrogen atmosphere was researched by high temperature dilatometer. And the influence of the particle size of W and green density on commence shrinkage temperature, sharp shrinkage temperature and shrinkage rate were also investigated. It shows that the commence shrinkage temperature and sharp shrinkage temperature of the compact with ultrafine grain are 970°C and 1240°C respectively. The maximum shrinkage rate is 0.11%/°C. The shrinkage ratio decreases with the increase of green density and increases with the increase of sintering temperature.
- 社団法人 粉体粉末冶金協会の論文
- 2003-11-15
著者
-
Lin Tao
Institute of Acoustics, Chinese Academy of Science
-
Lin Tao
Department Of Powder Metallurgy University Of Science And Technology Beijing
-
Lin Tao
Institute Of Acoustics Chinese Academy Of Science
-
Zhang Liying
Department Of Powder Metallurgy University Of Science And Technology Beijing
-
ZHANG Liying
Dept. Powder Metallurgy, University of Science and Technology Beijing
-
TAN Yuxin
Dept. Powder Metallurgy, University of Science and Technology Beijing
-
LIN Tao
Dept. Powder Metallurgy, University of Science and Technology Beijing
-
GUO Zhimeng
Dept. Powder Metallurgy, University of Science and Technology Beijing
-
WU Chengyi
Dept. Powder Metallurgy, University of Science and Technology Beijing
-
WU Qinghua
Dept. Powder Metallurgy, University of Science and Technology Beijing
-
GUO Zhimeng
Department of Powder Metallurgy, University of Science and Technology Beijing
-
WU Qinghua
Department of Powder Metallurgy, University of Science and Technology Beijing
-
Wu Qinghua
Department Of Powder Metallurgy University Of Science And Technology Beijing
-
Wu Chengyi
Department Of Powder Metallurgy University Of Science And Technology Beijing
-
Guo Zhimeng
Department Of Powder Metallurgy University Of Science And Technology Beijing
-
Tan Yuxin
Dept. Powder Metallurgy University Of Science And Technology Beijing
関連論文
- Progress of synthetic aperture sonar in China
- Di-(2-ethylhexyl) Phthalate Upregulates ATF3 Expression and Suppresses Apoptosis in Mouse Genital Tubercle
- Shrinkage Kinetics during Sintering W-Ni-Fe Heavy Alloy with Ultrafine Grain
- Effects of Bridged Particles on Compressibility of Nano-scaled Cemented Carbide Powder
- Role of Genetic Screening in a Chinese Woman of Childbearing Age with Hypertrophic Cardiomyopathy