Production of Co-B Alloy Powders by Chemical Reduction

スポンサーリンク

概要

• 論文の詳細を見る

• Co-B powders were prepared by chemical reduction. The powders had a spherical shape with an average diameter of about 0.1μm. X-ray diffraction and differential scanning calorimetry studies confirmed that the powders were amorphous. The amorphous powders showed lower saturation magnetization than the crystalline counterparts. Heat treatment of the powders above the crystallization temperature resulted in the formation of fcc Co, hcp Co, Co<SUB>2</SUB>B, and Co<SUB>3</SUB>B phases. The saturation magnetization of the annealed powders monotonically increased as the annealing temperature increased. On the other hand, the coercivity of the annealed powders rapidly increased with increasing annealing temperature. The powders annealed at 500°C had a saturation magnetization of 92 emu/g with a high coercivity of 1670 Oe.

• 社団法人 粉体粉末冶金協会の論文
• 2003-11-15

著者

• Saito Tetsuji

  Department Of Mechanical Engineering And Science Chiba Institute Of Technology

• Saito Tetsuji

  Department Of Mechanical Engineering And Science

• Saito Tetsuji

  Department of Applied Chemistry, Faculty of Engineering, Niigata University

関連論文

• Containerless Solidification of Undercooled Nd_2Fe_B by Electrostatic Levitation Furnace
• The Extraction of Sm from Sm-Co alloys by the Glass Slag Method
• Microstructures and Magnetic Properties of Nd-Fe-B-X (X =Co, Zr) Alloys Produced by a Metallic Mold Casting Method
• Microstructure of Nd-Fe-B Alloys Solidified under Microgravity Conditions
• Annealing of Amorphous Sm_5Fe_ Melt-Spun Ribbon
• Production of Co-B Alloy Powders by Chemical Reduction
• Magnetic Properties of Pr-Fe-Al Alloys Produced by the Metallic Mold Casting Method
• Microstructures and Magnetic Properties of Co-Zr System Alloys
• Catalytic hydrogenolysis of 1,1-difluoro-2-phenyl- and 1,1-difluoro-3-methyl-2-phenylcyclopropane.

スポンサーリンク