改良高炉スラグ細骨材を用いたプレミックスドライモルタルについて
スポンサーリンク
概要
- 論文の詳細を見る
The premix dry mortar was used as tile substrate mortar, tiling mortar, joint mortar for tiles and so forth. The granulated blastfurnace slag or the annealed blastfurnace slag could not use as fine aggregate for the premix dry mortar, because of the poor workability.In order to improve of the workability of mortar using the granulated blastfurnace slag as fine aggregate, a disintegration process was applied. The mortar tests using processed blastfurnace slag, non processed one and natural sand as fine aggregate were investigated. The workability of mortar using processed one was better than non processed one, and was similar to natural sand. Bending strength and compressive strength of mortar specimen were higher than non processed one and natural sand one. From these experiments, it was confirm that these processed blastfurnace slag could use as fine aggregate for the premix dry mortar.
- 社団法人 資源・素材学会の論文
- 2002-06-25
著者
関連論文
- スコリア溶融物の結晶化と物性に及ぼす添加物(ショ糖,CaO,MgO,SiO_2)の影響
- VあるいはWをドープしたTiO_2被覆中空ガラス球の製造と光触媒の特性
- シラス微粒中空ガラス (特集 加工技術が引き出すガラス系素材の新機能)
- 改良高炉スラグ細骨材を用いたプレミックスドライモルタルについて
- 改良高炉スラグ細骨材を用いたプレミックスモルタルについて
- 阿蘇黄土によるダイオキシン除去技術の開発
- アルミナ水和物被覆火山ガラス微粒子の加熱発砲性(2)
- 微粒中空ガラスフィラ-製造プロセスおよび装置の検討
- アルミナ水和物被覆火山ガラス微粒子の加熱発泡性
- シラス中の火山ガラスの加熱発泡性について
- 光触媒としての酸化チタン被覆微細中空ガラス球の応用
- 微粒シラスバルーン-セメント系コンパウンドの押出成形性
- 酸化チタン被覆微細中空ガラス球の調製
- Tetra-n-Butoxy Titaniumからの加水重合体の加熱分解法による酸化チタン被覆中空シラス球状体の開発
- チタニア水和物を被覆した微粒火山ガラスを原料とするTiO_2被覆微細中空ガラス球の調製