Design of Molten Salt Bath on the Basis of Acid-Base Cooperative Reaction Mechanism.Smooth Electrodeposition of Tungsten from KF-B2O3-WO3 Molten Salt (特集 New Trends in Molten Salt Chemistry and Electrochemistry)
スポンサーリンク
概要
著者
-
香山 滉一郎
Department of Materials Science and Engineering, Faculty of Engineering, Himeji Institute of Technol
-
森下 政夫
Department Of Mateials Science University Of Hyogo
-
Koyama Koichiro
Department Of Materials Science And Engineering Faculty Of Engineering Himeji Institute Of Technolog
-
Koyama Koichiro
Department Of Marterials Science And Engineering Faculty Of Engineering Himeji Institute Of Technolo
-
Morishita Masao
Department Of Materials Science And Chemistry Graduate School Of Engineering University Of Hyogo
-
Morishita Masao
Department Of Materials Science And Engineering Faculty Of Engineering Himeji Institute Of Technolog
-
UMEZU Takayuki
Department of Materials Science and Engineering, Faculty of Engineering, Himeji Institute of Technol
-
Umezu Takayuki
Department Of Materials Science And Engineering Faculty Of Engineering Himeji Institute Of Technolog
-
梅図 隆行
Department of Materials Science and Engineering, Faculty of Engineering, Himeji Institute of Technology
関連論文
- 連続鋳造の廃熱を利用した鉄鋼スクラップの予熱過程解析
- 連続鋳造過程の余熱による鉄鋼スクラップ予熱過程の基礎解析
- コークス、木炭、グラファイトのガス化反応性と気孔構造
- 溶鋼表面への鉄鉱石粉末吹きつけによる同時脱炭・脱窒反応のメカニズム(革新的高効率混合・分離リアクターの開発)
- (Fe,Al)_2O_3からCO-CO_2で還元されたAl_2O_3分散鉄の微細組織(製鉄)
- (Fe, Al)_2O_3のCO-CO_2ガス還元過程における生成物の微細組織
- メタケイ酸ナトリウム-o-クレゾール-4-スルホン酸水溶液におけるマグネシウムの陽極酸化
- コークス・木炭・グラファイトのガス化反応性と微細孔径分布
- 黒鉛を用いた鉄鉱石の炭素熱還元による金属焼結鉄の作製と熱力学的考察
- 各種炭素材料のガス化反応と炭素原子間の結合様式
- 弱酸化性ガスインジェクションによる溶銑の脱珪処理プロセスの開発
- 2価アルコール添加1-エチル-3-メチルイミダゾリウムブロミド : 臭化亜鉛溶融塩を用いるZnの電解(E)
- 連続鋳造過程の余熱による鉄鋼スクラップ予熱過程の基礎解析
- Relative Partial Molar Gibbs Energy of Magnesium Component Substituted into Zinc Site in the Mg-Zn Binary Compounds
- チタン、チタン合金の直接電解製造--液体金属の電析は可能か?
- 弱酸化性ガス吹き込みによる溶鉄の脱珪と脱炭(製鋼)
- 素材製造プロセス研究の夢
- SUS304ステンレス鋼中スピネル介在物生成のスラグ組成による制御(製鋼)
- SUS304ステンレス鋼スラブ中のスピネルを含む介在物の生成機構(製鋼)
- 溶融塩化物での不均化反応を用いたチタン合金コーティング
- 溶融塩中でのLaを含むMg金属の直接電析とその耐食性
- 炭材反応の高速化-炭材のガス化反応性と構造
- 溶鋼中へのH_2吹込みによる各種製綱反応の可能性(革新的高効率混合・分離リアクターの開発)
- ラマン分光法によるコークス、及び炭素材料の構造評価
- Effect of Cu on the Corrosion Resistance of a NiMo_2B_2-Dispersed Ni-Based Alloy
- NI_3B分散Ni基合金のHCI水溶液中での耐食性に及ぼすCu添加の効果
- NiMo_2 B_2分散Ni基合金の耐食性に及ぼすCu添加の効果
- La_Sr_XCoO_の熱容量測定
- Standard Gibbs Energy of Formation of Mg_3La Determined by Solution Calorimetry and Heat Capacity Measurement from Near Absolute Zero Kelvin
- エチレングリコール溶媒からのZn-Sb合金膜の電析
- La_Sr_XFeO_の絶対零度付近から高温までの熱容量測定
- Determination of Standard Gibbs Energy of Formation of Al_2Nd by Solution Calorimetry and Heat Capacity Measurement from Near Absolute Zero Kelvin
- Standard Gibbs Energy of Formation of Zn_8La Determined by Solution Calorimetry and Measurement of Heat Capacity from Near Absolute Zero Kelvin
- 熱力学諸量の測定とその結果を用いた化学熱力学計算によるNi-Mo-BおよびNi-W-B 3成分系状態図の決定
- La1-xSrxFeO3-δの絶対零度付近から高温までの熱容量測定
- Ni - M_3B_2 (M=Ni, Mo, Cr, W)合金の耐摩耗性および曲げ強度
- Ni-Mo-B-O 系の相関係図の作成と Ni-NiMo_2B_2 2 相合金の酸化特性の検討
- Ni-NiMo_2B_ 2相合金の硝酸と塩酸の混合水溶液中での耐食性に及ぼすCrとCu添加の効果
- Ni-NiMo_2B_2 2相合金のHNO_3水溶液中での耐食性に及ぼすCr添加の効果
- Calculated Phase Diagram of the Ni-W-B Ternary System
- Theoretical Study of Si K_β X-ray Fluorescence Spectrum of SiO_2-Na_2O Binary Slag by DV-Xα Molecular Orbital Calculation
- Self-Healing Ability of Zinc-Plated Steel Coated with Magnesium Electrodeposited from a Molten Salt
- Inhibition of Anodic Dissolution of Zinc-plated Steel by Electrodeposition of Magnesium from a Molten Salt
- SiO2-Na2O2成分系スラグのEPMAスペクトルの測定とその結果の分子軌道法による解釈
- Electronic States of Oxygen Ions of Molten Slags Used for Iron and Steel Making
- LiCl-KCl-MgCl_2系のMgCl_2低濃度側の状態図
- 反応焼結による新しいAl-Ti-N系合金の作製(第4報)-機械的性質の検討-
- 噴霧乾燥法による希土類酸化物分散タングステン粉末の作製と通電焼結
- 酸化物融体からのモリブデンの平滑電析〔英文〕
- Improvement in the Corrosion Resistance of Zinc-plated Steel by Electrodeposition of Magnesium from a Molten Salt
- Design of Molten Salt Bath on the Basis of Acid-Base Cooperative Reaction Mechanism.Smooth Electrodeposition of Tungsten from KF-B2O3-WO3 Molten Salt (特集 New Trends in Molten Salt Chemistry and Electrochemistry)
- Heat Capacity of La_Sr_XFeO_ from 2K to 1340K
- Preparation of White Heart Malleable Cast Iron in Na_2O-K_2O-SiO_2 Oxide Molten Salt
- Preparation of White Heart Malleable Cast Iron in Na_2O-SiO_2 Oxide Molten Salt
- 黒鉛を用いた鉄鉱石の炭素熱還元による金属焼結鉄の作製と熱力学的考察
- Indexing of X-ray powder diffraction data for potassium hexafluorovanadate(III).