- Fundamental Investigations on Solidification Crack Susceptibility for Weld Metals with Trans-Varestraint Test
- Effect of Sulphur on Solidification Cracking in Weld Metal of Steel (Report 6) : Weld Solidification Crack Susceptibility of High Tensile Low Nickel Alloy Steel
- Effect of Sulphur on Solidification Cracking in Weld Metal of Steel (Report 5) : Sulphide and Solidification Crack Susceptibility in Fe-S-Mn-Ni and Fe-S-Mn-C Quarternary Alloy Steels
- Effect of Sulphur on Solidification Cracking in Weld Metal of Steel (Report 2) : Theoretical Investigation on Change in Liquid Composition among Primary Crystals during Weld Solidification and on New Parameter Replacing Mn/S in Fe-S-Mn Alloy Steel
- Effect of Sulphur on Solidification Cracking in Weld Metal of Steel (Report 3) : Applicability of New Parameter Mn^3/S to Weld Metal of Fe-S-Mn Alloy Steel