Drastic suppression of the optical reflection of flash-lamp-crystallized poly-Si films with spontaneously formed periodic microstructures
スポンサーリンク
概要
- 論文の詳細を見る
Polycrystalline Si (poly-Si) films formed by flash lamp annealing of precursor a-Si films on glass substrates have periodic surface roughness spontaneously formed through crystallization, which effectively acts to decrease optical reflection. The surface roughness initially decreases, and then reversely increases with increase in the duration of wet etching, performed to modulate the surface morphology and to reduce optical reflectance. This curious phenomenon can be understood as the selective removal of surface projections, which contain a number of voids, and as different etching rates of large-grain and fine-grain regions. The antireflection effect is enhanced not by the variation of the surface roughness, but rather by the removal of the voids near the surface. The etched poly-Si films covered with antireflection films show remarkably low average reflectance of 3% without any complicated texturing processes, which will lead to the fabrication of high-efficiency solar cells by a simple process.
- Elsevierの論文
Elsevier | 論文
- Design and operation of an air-conditioning system fueled by wood pellets
- A comparative study of Al and LiF:Al interfaces with poly (3-hexylthiophene) using bias dependent photoluminescence technique
- Evidence of photoluminescence quenching in poly(3-hexylthiophene-2,5-diyl) due to injected charge carriers
- Volume shrinkage dependence of ferromagnetic moment in lanthanide ferromagnets gadolinium, terbium, dysprosium, and holmium
- In vivo promoter analysis on refeeding response of hepatic sterol regulatory element-binding protein-1c expression