微量の硫黄を添加したFe-20Cr-4Al合金の1273Kにおける長時間酸化
スポンサーリンク
概要
- 論文の詳細を見る
- 2002-07-31
著者
-
AMANO Tadaaki
Department of Materials Science and Engineering, Shonan Institute of Technology
-
ISOBE Hisao
Department of Materials Science and Engineering, Shonan Institute of Technology
-
MITANI Takashi
Department of Radiology, Osaka Rosai Hospital
-
Mitani Takashi
Department Of Materials Science And Engineering Shonan Institute Of Technology
-
OHISHI Masakazu
Department of Applied Physics, Okayama University of Science
-
Isobe Hisao
Department Of Materials Science And Ceramic Technology Shonan Institute Of Technology
-
Amano Tadaaki
Department Of Materials Science And Engineering Shonan Institute Of Technology
-
Amano Tadaaki
Department Of Materials Science And Ceramic Technology Shonan Institute Of Technology
-
Ohishi Masakazu
Department Of Materials Science And Engineering Shonan Institute Of Technology
-
Ohishi Masakazu
Department Of Applied Physics Faculty Of Science Okayama University Of Science
-
SAWAGUCHI Ryouta
Department of Materials Science and Engineering, Shonan Institute of Technology
-
Sawaguchi Ryouta
Department Of Materials Science And Engineering Shonan Institute Of Technology
関連論文
- 微量のYを添加したFe-20Cr-4Al-S(748ppm)合金の1273Kにおけるサイクル酸化挙動
- Case Report* MR Appearance of Hemangiopericytoma of the Thigh
- 微量の硫黄および活性元素(Y, Hf)を添加した耐熱合金の1373Kにおける1800ks間酸化
- 微量の硫黄を添加したAl_2O_3形成耐熱合金の1373および1473Kにおける高温酸化
- 微量の硫黄および活性元素を添加したAl_2O_3形成耐熱合金の1373および1473Kにおける高温酸化
- 液体窒素または空気中で冷却したAl_2O_3形成耐熱合金の酸化皮膜の剥離
- 微量の硫黄および活性元素を添加したFe-20Cr-4Al合金の1573Kにおける長時間酸化
- 微量の硫黄を添加した耐熱合金の高温酸化挙動
- 微量の硫黄を添加したFe-20Cr-4Al合金の高温酸化における硫黄の挙動
- 微量の硫黄および活性元素(Y, Hf)を添加した耐熱合金の1273Kにおける1800ks間酸化