熔接用諸鋼材の連続冷却変態図(第 6 報) : 60kg/(mm)^2 高張力鋼について
スポンサーリンク
概要
- 論文の詳細を見る
In the previous reports, the continuous cooling transformation diagrams were constructed for many mild steels and Mn-Si type high tensile steels. In this report, the continuous cooling transformation diagrams in case of maximum heating temperature 1350℃ have been constructed for steels containing a small quantity of Ni, Cr, Mo, V and Ti in addition to Mn and Si and having ultimate tensile strength of about 60kg/(mm)^2. The field of the intermediate structure (Zw) in the continuous cooling transformation diagrams of this type of steel is extending through an extremely long range of cooling time, differing from those of mild steels and Mn-Si type high tensile steels. This fact is considered to be relating to the high tensile strength and excellent weldability of this kind of steel. The effect of carbon content on critical cooling times for these types of high tensile steel is remarkable, as well as the case of mild steels and Mn-Si type high tensile steels. The critical cooling times C_z', C_f', C_p' and 50% martensite cooling time of steel YF containing 0.18% C differ remarkably from those of steel YG containing 0.11% C. If the carbon content of this type of steel is as low as that of steel YG, critical cooling times C_z', C_f', C_p' and 50% martensite cooling time of that steel have a tendency to approach to those of mild steel.
- 1959-11-25
論文 | ランダム
- C-04 仮名特異的な読字障害を示す左利き左大脳基底核損傷例(研究発表C,VII.第19回大会発表要旨)
- 右へならえ なんて言わないで--「左利き」1200万人のニューウェーブ
- 市民のページ 左利き(左党)
- 左利きと右利き
- 探偵クラブかがく班(18)なんで左利きがいるの?