Effects of Fluorination on Surface Charge Accumulation and Decay of Polyimide Film

スポンサーリンク

概要

• 論文の詳細を見る

• In this paper, we present a study aimed at clarifying the effects of fluorination time on surface charge accumulation and decay behaviors of fluorinated polyimide films. The samples were surface-fluorinated in a laboratory vessel at about 328 K using a F<inf>2</inf>/N<inf>2</inf>mixture with 20% F<inf>2</inf>by volume at 0.05 MPa for 15, 30, 45, and 60 min. Corona charging tests were performed at room temperature with a relative humidity of {\sim}40%. The chemical composition of the fluorinated layer of the samples was observed. The results indicate that charge density and charge decay rate are markedly affected by fluorination and that the degree of fluorination is affected by treatment duration.

• 2013-12-25

著者

• Li Jie

  School Of Life Sciences Tsinghua University

• Du Heng

  School of Electrical Engineering and Automation Tianjin University, Tianjin 300072, China

• Du Boxue

  School of Electrical Engineering and Automation Tianjin University, Tianjin 300072, China

• Li Jie

  School of Electrical Engineering and Automation Tianjin University, Tianjin 300072, China

関連論文

• Synthesis of Horn-Like BN Derived from Thorn-Like Ca_2B_2O_5・H_2O
• High-yield Synthesis of Boron Nitride Nanotubes by Annealing Fe_3BO_6
• HSulf-1 inhibits cell proliferation and invasion in human gastric cancer
• Effects of Fluorination on Surface Charge Accumulation and Decay of Polyimide Film

スポンサーリンク