Mn-Doped BaTiO3 Thin Film Sintered Using Nanocrystals and Its Dielectric Properties
スポンサーリンク
概要
- 論文の詳細を見る
BaTiO3 thin films homogeneously doped with Mn were prepared by a novel powder-sintering thin-film process. Mn-doped BaTiO3 nanocrystals 5–7 nm in diameter were synthesized by a sol–gel method and sintered to form a highly densified microstructure containing columnar grains epitaxially grown on a (111)-oriented Pt/TiO2/Al2O3 substrate at a low temperature of 800 °C. On the basis of the results of various structural analyses, Mn was suggested to act as an acceptor in the perovskite structure of BaTiO3, which was also supported by the experimental finding indicating that the leakage current density was significantly improved compared with that of a nondoped BaTiO3 thin film. Moreover, the dielectric constant of the Mn-doped BaTiO3 thin film, 728 at 10 kHz with a loss tangent of 1.3%, was higher than that of the nondoped BaTiO3 thin film, probably owing to the electrostrictive effect induced by in-plane tensile stress. These results clearly indicate the feasibility of using doped BaTiO3 nanocrystals in the powder-sintering thin-film process for improving dielectric properties.
- 2009-11-25
著者
-
Imai Hiroaki
Department Of Applied Chemistry Faculty Of Science And Technology Keio University
-
Mizuno Youichi
Research and Development Laboratory, Taiyo Yuden Corporation, 5607-2 Nakamuroda-machi, Takasaki, Gunma 370-3347, Japan
-
Suzuki Toshimasa
Research and Development Laboratory, Taiyo Yuden Corporation, 5607-2 Nakamuroda-machi, Takasaki, Gunma 370-3347, Japan
-
Kobayashi Keisuke
Research and Development Laboratory, Taiyo Yuden Corporation, 5607-2 Nakamuroda-machi, Takasaki, Gunma 370-3347, Japan
-
Takezawa Yoko
Research and Development Laboratory, Taiyo Yuden Corporation, 5607-2 Nakamuroda-machi, Takasaki, Gunma 370-3347, Japan
-
Nakasone Fumi
Research and Development Laboratory, Taiyo Yuden Corporation, 5607-2 Nakamuroda-machi, Takasaki, Gunma 370-3347, Japan
関連論文
- Epitaxial Growth of Wurtzite ZnO Crystals in an Aqueous Solution System
- Epitaxial growth of winding ZnO nanowires on a single-crystalline substrate(Aqueous Solution Science for Ceramic Processing II)
- Preparation of Porous SnO_2 Particles Having High Specific Surface Area and High Thermal Stability via an Aqueous Solution Route and Subsequent Hydrothermal Treatment
- Incorporation of Dyes into Silica-Surfactant Mesostructured Nanoparticles as a Nanoscale Host Material for Organic Molecules
- A Biomimetic Approach for Hierarchically Structured Inorganic Crystals through Self-Organization
- Photochemical Reactions in Nanoscopic Organic Domains Generated from Oriented Crystals with Polymers : Nanocrystalline Mosaics as a New Family of Host Materials
- Development of Ordered Calcium Carbonate Microarrays from Polymorph Specific Planar Films
- Formation of Silicate-mediated CaCO_3 Films
- Nanoscale morphological design of ZnO crystals grown in aqueous solutions
- Phosphate-mediated ZnO Nanosheets with a Mosaic Structure
- Biomimetic Approach for Exact Control of TiO_2 Periodic Microstructures
- Preparation of Hollow Fibers of Tin Oxide with and without Antimony Doping
- Photoreduction of Amorphous and Crystalline ZnO Films(Surfaces, Interfaces, and Films)
- Mn-Doped BaTiO3 Thin Film Sintered Using Nanocrystals and Its Dielectric Properties
- Effects of Titania Surface Orientation on the Heterogeneous Formation of Barium Titanate by Hydrothermal Synthesis
- Nanoparticle-Sintered BaTiO3 Thin Films and Its Orientation Control by Solid Phase Epitaxy
- Fabrication of Rutile TiO_2 Foils with High Speciffic Surface Area via Heterogeneous Nucleation in Aqueous Solutions
- Versatile Modification for Highly Dispersive and Functionalized Mesoporous Silica Nanoparticles
- Self-organization of hollow-cone carbonate crystals through molecular control with an acid organic polymer