Mechanism of Properties of Noble ZnS–SiO2 Protection Layer for Phase Change Optical Disk Media

概要

論文の詳細を見る
A ZnS–SiO2 composite dielectric is widely used in the optical stack designs of rewritable optical recording media as an index-matching medium and as a protection layer for the high-index chalcogenide (compound with sixth group element of S, Se, Te) phase change material used in these media. The addition of Si and O to ZnS is primarily intended to stabilize against crystalline grain growth of ZnS with high numbers of direct overwriting cycles. In this study, we carry out infrared (IR) spectroscopy to clarify the role of Si in this stabilization process. IR spectroscopy is performed on sputter as-deposited and annealed ZnS–SiO2 dielectric protection layers. We find that Si exists not in the SiO2 oxide phase but as [SiS4-nOn] tetrahedrons. Moreover, zinc and sulfur do not exist as ZnS, but in highly chemically disordered ZnS:O crystallites. The highly directional and rigid covalent bonds in the [SiS4-nOn] tetrahedrons are key to establishing thermal stability against the coalescence of ZnS. The importance of the Si–S bond also extends into a more thorough understanding of the low thermal conductivity of the ZnS–SiO2 material. The consideration of elastic implications allows us to predict an average phonon velocity less than 50% compared to that in SiO2. With this, we predict a thermal conductivity of 0.0067 W cm-1 K-1 for this material, which is in complete agreement with measured values.
2006-08-15