Annealing and Aging Effect in 0.95 Pb(Zr0.52Ti0.48)O3–0.05 NiFe1.9Mn0.1O4 Particulate Magnetoelectric Composites

スポンサーリンク

概要

• 論文の詳細を見る

• The results in this letter show the possibility of realizing a high magnetoelectric (ME) coefficient material by synthesizing the particulate composites of ferroelectric and ferromagnetic components using the annealing and aging treatment. The ME composites were fabricated using a combination of conventional mixed oxide sintering and thermal treatment. The thermal treatment constituted of annealing at temperature closer to calcination temperature (${\sim}800$°C) followed by aging at lower temperatures (300–400°C). Microstructure of the fabricated samples was analyzed using the X-ray mapping in scanning electron microscopy (SEM) and it was found that NiFe1.9Mn0.1O4 (NFM) is distributed inside the Pb(Zr0.52Ti0.48)O3 (PZT) grains on the length scales of 100 nm. The magnitude of piezoelectric constant ($d_{33}$) and the dielectric constant exhibited significant variation with aging time and temperature. It was found that the magnitude of ME coefficient for PZT–5NFM sample increased from 37 to 56 mV/cm$\cdot$Oe after thermal treatment, an enhancement of ${\sim}50$%.

• INSTITUTE OF PURE AND APPLIED PHYSICSの論文
• 2006-02-25

著者

• Priya Shashank

  Material Science And Engineering University Of Texas At Arlington

• Islam Rashed

  Material Science And Engineering University Of Texas At Arlington

• Priya Shashank

  Material Science and Engineering, University of Texas at Arlington, Arlington, TX 76019, U.S.A.

関連論文

• Annealing and Aging Effect in 0.95 Pb(Zr_Ti_)O_3-0.05 NiFe_Mn_O_4 Particulate Magnetoelectric Composites
• Modeling of Piezoelectric Energy Harvesting Using Cymbal Transducers
• Piezoelectric Windmill: A Novel Solution to Remote Sensing
• Annealing and Aging Effect in 0.95 Pb(Zr0.52Ti0.48)O3–0.05 NiFe1.9Mn0.1O4 Particulate Magnetoelectric Composites

スポンサーリンク