高クロム鋼の長時間材料特性に及ぼす微量タングステン添加量の影響

スポンサーリンク

概要

• 論文の詳細を見る

• The applicability of high chromium (Cr) steel as the main structural material in fast breeder reactors (FBR) has been explored to enhance the safety, the credibility and the economic competitiveness of FBR power plants. Tungsten (W) is believed to improve the high temperature strength of high Cr steels by solid-solution strengthening mechanism, although the long-term effectiveness and stability of such a strengthening mechanism has not fully been understood yet. High Cr steels controlling W content are produced and tensile tests, creep tests, aging tests and charpy impact tests were conducted to investigate the long-term material properties. It was observed that the short-term creep strength could be improved by W. However, there is almost no influence of W on the long-term creep strength. And it was observed that the impact properties after aging could be improved by decreasing of W. It was found that the optimal W content for excellent high Cr steel of FBR grade are < 0.1 wt. %, under FBR operating conditions.

• 日本鉄鋼協会の論文

著者

• 鬼澤 高志

  日本原子力研究開発機構次世代原子力システム研究開発部門FBR要素技術ユニット炉心・構造材料グループ

• 永江 勇二

  日本原子力研究開発機構次世代原子力システム研究開発部門FBR安全評価ユニット構造材料評価グループ

• 菊地 賢司

  茨城大学大学院フロンティア応用原子科学研究センター

関連論文

• 高クロム鋼におけるMX析出強化の長時間安定性・有効性の検討(相変態・材料組織)
• 616 ヒステリシスエネルギーによる316FR鋼のクリープ疲労寿命評価(高温低サイクル疲労・クリープ疲労,高温環境下における材料の変形・損傷・破壊,オーガナイスドセッション2)
• 高クロム鋼の長時間材料特性に及ぼす微量タングステン添加量の影響

スポンサーリンク