脱炭処理した球状黒鉛鋳鉄におけるパーライトリングの生成機構
スポンサーリンク
概要
- 論文の詳細を見る
During the cooling of a spheroidal graphite cast iron specimen to room temperature after decarburization at 973 to 1373 K, a decarburized layer and pearlite layer were found to form parallel to the surface of the specimen. In the case of rod shaped specimens, the pearlite layer showed a ring-like shape in the cross-section of the specimen, and so was termed "pearlite-ring". The width of the pearlite-ring increased with increasing depth of the decarburized layer, and also with increasing decarburizing temperature and decarburizing time. The width had a tendency to increase with increasing cooling rate after decarburization. From the results of EDS analysis and microstructure observation on formation behavior of the pearlite-ring, the formation mechanism is considered as follows : In the decarburized layer, there are some voids without any graphite, other voids with residual graphite and a distribution of dissolved carbon concentration decreasing from the inner side to surface side in the specimen. Since the γ austenite structure during decarburization transforms to a α ferrite structure with low solubility for dissolved carbon concentration, during cooling from γ to α, the supersaturated dissolving carbon atoms should precipitate as Fe3C in the matrix or as C on the residual graphite in the voids. In the decarburized region having suitable dissolved carbon concentration and voids without any residual graphite, the carbon atoms in the matrix precipitate as Fe3C to form pearlite structure. Therefore, the forming position of the pearlite-ring strongly depends on the cooling rate after decarburization in connection with the diffusion rate of carbon atoms in the matrix.
- Japan Foundry Engineering Societyの論文
Japan Foundry Engineering Society | 論文
- 球状黒鉛鋳鉄の延性破壊に及ぼす応力３軸度及び基地組織の影響
- 紡織機鋳物の鋳造法に就いて (其の一)
- 光ファイバで紫外線を導光した光造型機の開発と石こう鋳造への適用
- 薄肉球状黒鉛鋳鉄の黒鉛粒数に及ぼす元湯硫黄量，冷却速度及び希土類元素添加時期の影響
- Fe-Si合金及びFe-C-Si合金の塩浴窒化に及ぼすSiの影響とFe，Siの窒化物について