Preparation and Properties of Thermoplastic-resin-based Nanocomposites for the Development of Esthetic Orthodontic Wires
スポンサーリンク
概要
- 論文の詳細を見る
Transparent PMMA/layered silicate nanocomposites were fabricated by a solution intercalation method. Montmorillonite (MMT), organically modified with alkylammonium ions, was selected as the filler for reinforcement. Platelets of organically modified MMT were well-dispersed macro-scopically in dissolved PMMA. X-ray diffraction patterns showed that a peak regarded as a basal spacing was shifted toward the lower 2θ values, indicating a diffusion of PMMA polymer chains into interlayer regions of MMT. TEM micrographs revealed well-intercalated and partially exfoliated structures of organically modified MMT. Board-shaped specimens used for flexural tests were fabricated by compression molding at 230°C. The specimens were transparent enough for their use as esthetic orthodontic wires. The flexural modulus of the nanocomposites increased marginally, relative to that of PMMA, with the increasing amount of clay.
- ナノ・バイオメディカル学会の論文
ナノ・バイオメディカル学会 | 論文
- Effects of Nano-hydroxyapatite Content on Bone Formation in Nano-hydroxyapatite-collagen Composite Membrane with BMP-2 Application
- Effect of Crosslinking Agent in Nanohydroxyapatite-collagen Composite on Ectopic Bone Formation with BMP-2 Application
- An Evaluation of Fluorescent Orthodontic Adhesives Containing Eu-doped ZnO at Room Temperature
- Introduction of Rare-Earth-Element- Containing ZnO Nanoparticles into Orthodontic Adhesives
- Evaluation of Protein Adsorption to Carbon Nanotubes having Different Property, and Identification of Adsorbed Proteins