A Study of Degradation Mechanism of Alginate by Gamma-irradiation
スポンサーリンク
概要
- 論文の詳細を見る
Alginate of an average molecular weight(M<SUB>w</SUB>) of approx. 900kDa with the ratio of M(mannuronate)/G(guluronate)about 1.3 in aqueous solution was irradiated with <SUP>60</SUP>Co gamma-rays at doses up to 800kGy. With the increase of the irradiation dose Mw of irradiated products was reduced and the dose was correlated with the molecular weight distribution of degraded products. The new bands appeared at 265 nm and 1709cm<SUP>-1</SUP> in UV and FTIR spectra of irradiated alginate suggested that the scission was accompanied by side reactions leading to the formation of carbonyl groups. The chemical analysis proved the increase of carboxyl groups and reduction of reducing groups of irradiated alginate. The NMR spectra indicated not only the formation of carbonyl groups but also the generation of unsaturated product with C<SUB>1</SUB> and C<SUB>4</SUB> double bonds at nonreducing terminal and reducing end product. The degradation mechanism of alginate by irradiation was proposed.
- 公益社団法人 日本アイソトープ協会の論文
公益社団法人 日本アイソトープ協会 | 論文
- Improvement of a Gas Scintillation Proportional Counter
- Questionnaire Survey of SPECT Studies after the Supply Shortage of Tc-99m and Model Analysis Concerning Earnings and Expenditure of Generator Use
- 各種骨病変検出における臨床的有用性と医療経済効果に関する骨シンチグラフィと｀１８´Ｆ－ｆｌｕｏｒｉｄｅ ＰＥＴの比較検討
- Combination of Sulfur Isotope Ratio of Non-sea Salt Sulfate and Lead-210 Concentration in Aerosols as an Index of Long-range Transported Aerosols
- 放射線生物学の動向