プロジェクション形状改良による2024アルミニウム合金スタッド/5052アルミニウム合金薄板高速固相接合材の接合強度の向上
スポンサーリンク
概要
- 論文の詳細を見る
A 2024-T3 aluminum alloy stud with the circular ridge projection at the bottom was welded to a 1.5 mm-thick 5052-H34 aluminum alloy thin plate by the advanced high-speed solid-state joining method. The projection crushed and spread along the plate surface. Joining was achieved within a few milliseconds with a negligible temperature increase of the joint. Asymmetrical deformation occurred on both the inner side and the outer side of the projection. It was found that enlargement of the joining area outside of the projection was effective to increase the joint strength by the present authors' previous study. Based on this guide, in the present study, trial was made to increase the joint strength by determining the optimum projection shape at a bottom of the stud. Three types of projection shape were prepared and they were provided for joining tests at various discharge voltage conditions, and joint interface morphology, joining area and joint strength were compared. When we used the stud with which the projection tip shifted to the inner side, the outer side of the projection spread much wider along the plate surface than the inner side. This worked effectively to increase the joint area of the outside and the resultant joining strength. It is confirmed that the modified projection shape is useful for the stud welding for the thin plate.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.