Al–Mg合金およびAl–Si合金におけるAE法を用いた凝固割れ発生の判断基準
スポンサーリンク
概要
- 論文の詳細を見る
Detection of solidification cracking of JIS AC7A aluminum alloy and Al–7%Si alloy was attempted by using acoustic emission method. In order to detect AE of solidification cracking, we investigated about AE signals of gas porosity, shrinkage cavity, and fracture in the semi-solid tensile test. The frequency bands of these casting defects were 150 kHz or less, so the source characterization of AE signals were difficult by that. Therefore we discussed and suggested value of integrated AE peak volt as an indicator of crack initiation. As a result, we proved value of time integral (IAP) is beneficial for eutectic alloy and value of temperature integral (TIAP) is beneficial for noneutectic alloy. We also suggested value of time temperature integral (DIAP) as the criterion of crack initiation which is beneficial for eutectic and non-eutectic alloy.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.