合金元素を含んだ６０００系アルミニウム合金／鋼異種金属接合における界面反応層のナノインデンテーション測定
スポンサーリンク
概要
- 論文の詳細を見る
Nanoindentation measurements were successfully applied to the interfacial reaction layers in dissimilar metal joints of 6000 series aluminum alloys containing alloying elements to steel in order to characterize their mechanical properties. The nanoindentation hardness of the reaction layer formed at the aluminum side was lower than that formed at the low carbon steel (SPCE) side of the investigated joints. At the aluminum side, the nanoindentation hardness changed by the addition of alloying elements. The hardness of the resulting Al12Fe3Si intermetallic compound (IMC) (and the same IMC containing Cu) was lower than that of Al3Fe. In comparison with the hardness values obtained from bulk Al–Fe binary series IMCs, it is considered that hardness changes of interfacial reaction layers are derived from the crystal structural changes produced by the alloying elements. The result of micro-testing of Al–Fe series IMCs indicates that the modification of the interfacial reaction layer by alloying elements contributes to higher ductility and the improvement of joint strength through crystal structural change.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.