7075アルミニウム合金の摩擦攪拌接合継手のビッカース硬さに寄与する金属学的諸因子
スポンサーリンク
概要
- 論文の詳細を見る
Vickers hardness of friction stir welded 7075-T6 and 7075-O aluminum alloy plates were investigated. During welding, the tool rotation and tool traverse speeds were 1500 rpm and 300 mm/min, respectively. In order to study the anisotropy in the welded joints, the joints were welded in directions parallel and right angle to the rolling direction. Defect-free joints were obtained under the above condition. A fine and equiaxed recrystallised microstructure with grain size of approximately 3 μm was formed in the stir zone of the joints. Anisotropy in welded joints along the welding directions was not detected in terms of the microstructural characteristics of the joints. After friction stir welding, the Vickers hardness of the stir zone of the T6 joints decreased, but that of the O joints increased. On the other hand, after natural aging for 5 months, the Vickers hardness of the stir zone of the T6 joints increased and closely reached the hardness level of the base metal, while the Vickers hardness of the stir zone of the O joints increased further. From the above-mentioned Vickers hardness distributions, no anisotropy was observed along the welding direction. The above-mentioned behavior in hardness of the joints was discussed briefly on the basis of the Hall-Petch relation as well as other strengthening mechanisms.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.