AZ31マグネシウム合金における鏡面光沢度に対する表面粗さの影響
スポンサーリンク
概要
- 論文の詳細を見る
In order to clarify the relationship between the surface roughness and the metallic luster and the relationship between the surface roughness and the conditions of the surface treatment, the surface roughness was examined in AZ31 magnesium alloy. The standard state of the metallic luster was the surface polished by emery paper #2000. The surface roughness and the metallic luster were quantified by the root mean square roughness, σ, with a cutt-off value of 0.002 mm and the specular gloss. It was analyzed the relationship between the metallic luster and the surface roughness. For the result, the metallic luster was available that the surface roughness was formed in the range of 0<σ/λ<0.1, and the necessary value of σ for the realization of the metallic luster was less than 53 nm. The optimal acid aqueous solution treatment was available the metallic luster, and σ was 9 nm. Finally, σ with the surface treatment conditions in the both component included the oxidant and high temperature and in the oxidant-free both components was examined, and was about 80 nm. Therefore, it was concluded that the metallic luster was unavailable.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.