AE法を用いたAl‐7 mass%Si合金の凝固割れ検知のためのAE信号の分離
スポンサーリンク
概要
- 論文の詳細を見る
Detection of solidification cracking of Al–7 mass%Si alloy was attempted by using acoustic emission method. According to our previous report, it was found that it is necessary to separate AE of solidification cracking from other estimated sources such as gas porosity, shrinkage cavity, or eutectic solidification to detect AE of solidification cracking. Then, we investigated about AE signals of gas porosity, shrinkage cavity, and eutectic solidification. As a result, AE of eutectic solidification was not generated or was too small to detect. AE of shrinkage cavity and gas porosity formation were detected at the start of eutectic solidification, and the frequency band was 150 kHz or less. The frequency band of AE accompanied with fracture of solidifying castings was also 150 kHz or less. Therefore, it was difficult to separate AE of solidification cracking from gas porosity, shrinkage cavity, or eutectic solidification by the frequency band. However, integrated AE peak volt during solidification correlated with crack ratio. When Solidification cracking occurred, Integrated AE peak volt was about more than 1000 V during solidification. In situ detection of solidification cracking will be possible by investigating integrated AE peak volt.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.