AZ61マグネシウム合金板の繰返し曲げ加工に伴う双晶形成が集合組織に及ぼす影響と成形性向上
スポンサーリンク
概要
- 論文の詳細を見る
Magnesium alloy is the lightest metal among structural metals being used today. However, because the rolled sheets of magnesium alloy are expensive and poor in press formability, the reduction of manufacturing costs and especially the improvement of formability are eagerly required. In order to overcome these problems, the dispersion of texture of rolled sheets caused by twin formation in repetitive bending at room temperature would be effective. In present experiment using the rolled sheets of AZ61 magnesium alloy, the relationship between the times of repetitive bending and the change of texture was investigated. In 4-times repetitive bending, the tensile twin formation and the dispersion of basal plane texture were observed by X-ray diffraction and SEM-EBSD analysis. As the result of formability test, severe 90° V shape bending (R/t=1) and nearly twice bulging formability were attained in comparison with those of conventional rolled sheets at 473 K. The results of this study suggest that the press formability of rolled sheets of AZ61 magnesium alloy would be effectively improved by repetitive bending at room temperature.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.