純アルミニウム/銅クラッド材接合部の強度と高分解能TEM組織
スポンサーリンク
概要
- 論文の詳細を見る
It is known that it is difficult to bond dissimilar metals such as aluminum and copper or aluminum and iron using diffusion bonding, because an intermetallic compound is easily produced at the bond interface and bonding strength becomes low. However it is possible to bond the dissimilar metals using the vacuum roll bonding which performs hot rolling in a vacuum. In this study, we investigated the effect of bonding temperature and reduction of aluminum plate thickness on bonding strength of Al/Cu clad materials when aluminum-clad copper (Al/Cu clad) materials were produced at 3 Pa in vacuum degree by the vacuum roll bondings. Bond tensile strength of Al/Cu clad materials increased as the reduction was increased. Their fracture types were classified according to the fracture pass, that is, in the base metal of the aluminum, at the bond interface of Al/Cu clad material or in the base metal and/or at the bond interface. Furthermore, the bond interfaces of Al/Cu clad materials were observed using a transmission electron microscope and an electron dispersive spectroscopy. As a result, it was clarified that Al/Cu clad materials are soundly produced using the vacuum roll bonding when thickness of diffusion layer is less than 60 nm even if intermetallic compounds were developed.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.