Mg96Zn2Y2合金チップ連続押出固化成形体の機械的性質
スポンサーリンク
概要
- 論文の詳細を見る
The authors examined the properties of Mg96Zn2Y2 alloy bars made through continuous consolidation of chip using a newly developed single screw extrusion machine designed for magnesium alloy chip. Surface conditions as well as microstructure of the consolidated Mg96Zn2Y2 alloy varied depending on the die conditions. With a die inner diameter of 49 mm and die temperature of 723 K, severe plastic deformation in the die produced a fine-grain microstructure in the consolidated Mg96Zn2Y2 alloy bar. The compounds such as Mg12YZn and Mg3Y2Zn3 in the bar were also dispersed finely. Owing to its randomized crystal orientation, a secondary extruded bar made from the consolidated Mg96Zn2Y2 alloy bar showed a higher ductility than that of ingot-extruded bar. The fine-grain consolidated Mg96Zn2Y2 alloy bar exhibited an elongation of 308% at 723 K. Furthermore, the deformation characteristics were examined with the consolidated Mg96Zn2Y2 alloy bar for the purpose of determining its suitability as hot-processing material billets. The fine-grain consolidated Mg96Zn2Y2 alloy bar was compressed without cracking up to 623 K while Mg96Zn2Y2 ingot cracked. It was found that smaller grain diameter made the m-value higher.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.