Mg96Zn2Y2合金インゴットおよびチップの押出における強化メカニズム
スポンサーリンク
概要
- 論文の詳細を見る
In order to make the effect of processing clear, Mg96Zn2Y2 alloy ingot and machined chips were extruded at various extrusion conditions. Tensile yield strength of extruded bar from ingot and extrusion force were increased with decreasing extrusion temperature. Tensile yield strength and extrusion force was proportional to hardness of ingot that is measured at extrusion temperature. Increased hot hardness resulted in improved strength with increasing of the degree of work hardening and extrusion force. Improvement of the degree of work hardens was observed as crystal orientation by XRD. Meanwhile, strain hardening of machined chips plays a major role of strengthening at extruded bar from chips. Static recrystallization of chips at preheating causes randomization of crystal orientation and higher elongation of extruded bar from chips. Difference in recrystallization behavior between extrusion of ingot and chips, dynamic recrystallization at ingot extrusion and static recrystallization at chips extrusion, was due to difference of strength mechanism of extruded bar from ingot and chips.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.