7075アルミニウム合金板摩擦攪拌接合継手の板厚方向の衝撃圧縮応力‐ひずみ応答
スポンサーリンク
概要
- 論文の詳細を見る
High strain-rate compressive stress–strain characteristics of AA7075-T651 and its welds as produced by the friction stir welding (or FSW) process are investigated using the conventional split Hopkinson pressure bar. Friction stir welded AA7075-T651 joints are made under a fixed set of welding conditions. Cylindrical specimens machined along the thickness direction of both the base material and the friction stir weld nugget region are used in the static and impact compression tests. The micro-hardness tests are conducted across the centerline of the friction stir welded AA7075-T651 joint in order to examine the microstructural change. It is shown that the compressive flow stress of the weld nugget is reduced to about 70 to 85% of that of the base material, and that both the base material and the weld nugget exhibit almost no strain rate effect up to nearly ε˙=103/s.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.