脱気した純水中のアルミニウムの腐食
スポンサーリンク
概要
- 論文の詳細を見る
The Amount of aluminum corrosion was critically measured in deoxidized pure water. It was indirectly calculated from the pressure of the hydrogen gas produced by the cathodic reaction. The accuracy of this device reached as high as 0.1 mg/m2. The corrosion rate of A1N99 (99.99% aluminum) was then examined and compared with the images taken by both scanning electron microscope (SEM) and transmission electron microscope (TEM). In particular, images of the surface were taken by SEM and that of the cross section by TEM. From these comparisons, a new corrosion mechanism was proposed; 1) aluminum corrosion starts by the formation of small pits with a diameter of about 0.1 μm, 2) the number of these small pits increases and spreads over the entire surface. In addition, there is a time-lag between the increase of hydrogen gas pressure and the formation of corrosion products on the surface. The most likely reason for this time lag is that the Al ions require a long period of time to form stable oxide films.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.