双ロール式鋳造圧延した6016アルミニウム合金板の耐糸錆性に及ぼすリップルマークの影響
スポンサーリンク
概要
- 論文の詳細を見る
Al-Mg-Si alloy strips were prepared by the twin roll cast (TRC) in order to investigate the effect of the ripple mark observed in the strips on filiform corrosion resistance after paint. The TRC strips have 1-2 micrometers segregation layer which included high concentration iron and silicon under the surface. In the dark portion of ripple mark, the concentration of iron and silicon in the layer were high. According to the results of the cyclic filiform corrosion test, the ripple mark decreased the corrosion resistance. In the case of the scalped strip, the corrosion resistance was improved. As a result, the ripple mark with the surface segregation layers of iron and silicon decreased the filiform corrosion resistances on TRC strips.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.