高配向性ラメラ組織を有するTi‐43mol%Al金属間化合物の創製とクリープ特性
スポンサーリンク
概要
- 論文の詳細を見る
Various processes consisting of high temperature deformation and heat treatment are experimentally examined on Ti-43mol%Al in order to control the lamellar arrangement in TiAl intermetallic compound. High temperature uniaxial compression in α+γ as well as α2+γ two phase state is effective to rotate the lamellar interface to the position parallel to the compression plane. The high temperature compression in α2+γ two phase state results in the formation of many cracks along the lamellar colony boundaries while no cracks are observed when the compression is made in the α+γ two phase state. Deformation in the two phase state deduce the formation of many single phase grains along the colony boundaries. It is found that the heat treatment at the temperature slightly higher than that for high temperature deformation in the α+γ two phase region is effective to eliminate the single phase grains. Compression creep tests are performed on two kinds of specimen having different lamellar arrangement; one has the lamellar interface parallel to the compression direction and the other has the interface inclined about 45° to the compression direction. The specimen having the lamellar interface parallel to the compression direction shows the creep rate much lower than that of the other.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.