Al‐Mg‐Sc合金におけるAl3Sc粒子のオストワルド成長
スポンサーリンク
概要
- 論文の詳細を見る
The Ostwald ripening of Al3Sc particles in an Al-1 mass% Mg-0.27 mass% Sc alloy aged at 673, 698 and 723 K has been investigated. The size of the particles was determined by transmission electron microscopy and the Sc concentration in the Al matrix by electric resistivity measurements. The transition from growth to coarsening is found to occur. The Al3Sc particles grow more slowly at the coarsening stage than at the growth stage. The coarsening rate is identical with that of Al3Sc particles in an Al-0.28 mass% Sc alloy. Application of the Lifshitz-Slyozov-Wagner theory has enabled us to calculate independently the matrix/Al3Sc interface energy γ and volume diffusion coefficient D of Sc in Al during coarsening of particles. The estimates of γ and D are in agreement with those derived by the same method from data on coarsening of Al3Sc particles in the Al-Sc alloy. Whether the particles are coherent or semi-coherent with the matrix, the value of γ is nearly 230 mJm-2.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.