Al‐Mg‐Si‐Cu合金圧延板の幅方向に連続した比抵抗変動
スポンサーリンク
概要
- 論文の詳細を見る
To study the bake-hardening behavior of Cu added Al-1%Mg2Si alloys by the tensile test after resistivity measurement, resistivity of many samples taken from a rolled sheet was measured in various stages of heat treatment. The resistivity ρSTQ in the 848 K-3.6 ks solution treated and water quenched state (STQ) fluctuated within ranges of 0.9 to 1.7 nΩm. There were good linear relations between the ρSTQ and resistivity after room temperature pre-aging for 1 day (ρRTP) for each of four alloys. The ρRTP values were maintained after short period final aging at 448 K. Possible causes of the fluctuation in ρ were checked. Effects of the STQ conditions on the ρSTQ were negligible. Because the Matthiessen plot of the ρRTP gave good straight lines having acceptable gradient, the fluctuation is not due to errors in size factor and resistance. Change in room temperature showed no correlation with increment up to the ρRTP. Therefore, it is concluded that the ρSTQ of rolled plates used in a series of study have a stripe shaped distribution of the ρSTQ ranging ±0.25 to 0.5 nΩm in the transverse direction with width of 10 to 20 mm extending about 360 mm in the longitudinal direction. In a rough estimation, this fluctuation in ρ is corresponding to variation in Mg, Si or Cu contents of ±0.05 to 0.15 mass% from analysed compositions, though the species of alloying elements is not clear.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.