純チタンおよびTiNコーティング面の光沢度と表面色に及ぼす表面粗さの影響
スポンサーリンク
概要
- 論文の詳細を見る
In this study, the effect of surface roughness on glossiness and surface color for a pure titanium and a TiN coating surface was investigated based on the experimental discussions. CIELAB (L*a*b* color system) was applied to the evaluation method of surface color. Specimens were machined so that the arithmetical mean roughness, Ra, is less than 1.0 μm. From the results of experiments, the arithmetical mean roughness, Ra, decreased, as the glossiness, Gs (60°), increased. Especially, the glossiness value in the roughness range Ra ≤ 0.2 μm was distributed from 50 to 400. Moreover, the arithmetical mean roughness, Ra, decreased, as the lightness, L*, and a, b chroma, C*ab, decreased. The TiN coated surface with vividness had a pronounced tendency to decreasing lightness, L*, and a, b chroma, C*ab. This was attributable to the smaller difference of elevation of the spectral reflectance curve by reason that the short wavelength was diffused more than the long wavelength.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.