Al‐Cu‐Si‐X系低融点ろう材の開発とセラミックとアルミニウム合金の接合
スポンサーリンク
概要
- 論文の詳細を見る
The development of a low-melting-point-braze based on the Al-Cu-Si ternary eutectic composition with Zn and the joining of Si3N4/Al alloy were investigated. The Al-27.1%Cu-4.7%Si-50%Zn alloy which has solidus point 687 K and liquidus point 699 K was made into the brazing foil using by a Rapid Quenching Device. The joining strength was obtained about 180 MPa at 773 K in the atmosphere of flowing N2. It was considered that Zn restrained to form the Al2Cu layer at the joining interface, because Zn made the copper solubility limit in aluminum increase and the copper diffusion into the aluminum alloy promote.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.