アルミニウム板のせん断加工特性に及ぼす側圧の影響
スポンサーリンク
概要
- 論文の詳細を見る
In order to improve sheared edge quality of aluminum sheets, shearing tests were conducted under various axial stresses at the shearing region, and the effect of the axial stress was investigated. Numerical simulations of the shearing process were carried out using a rigid plastic finite element simulation code developed by the authors. In the simulation, the Jeong expression was used as a fracture criterion of aluminum sheet. The distributions of fracture value and mean normal stress at the shearing region of the sheet were calculated. The experimental and simulation results showed that the rollover depth and fracture surface length decrease, but the burnish surface length increases with increasing additional axial compressive stress. When the axial compressive stress was applied, the mean normal stress becomes lower at the shearing region. Therefore, the fracture value was decreased, and the crack initiation was delayed. The experimental results were in good agreement with the simulation results.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.