アルカリ水溶液中におけるアルミニウム合金クラッド材の局部腐食
スポンサーリンク
概要
- 論文の詳細を見る
Aluminum alloy three-layered brazing sheets, clad with sacrificial anode alloy on one side of them, have widely been used for the tube of radiators for automotive in which cooling water circulates. Inner pitting corrosion resistance of the tube has been excellent both in acidified and in neutral corrosive aqueous solutions by the effect of sacrificial anode. On the other hand, it has been reported that the sacrificial anode does not work effectively in alkaline solution, and perforation by pitting corrosion occurs in earlier testing period of time. In this report, localized corrosion characteristics in alkaline solution were investigated by immersion corrosion tests and electrochemical measurements. Based on the experimental results, new corrosion mechanism was proposed in terms of solution environment formed on cathode surface. Pitting corrosion of the core alloy grew not with the attack by the alkaline bulk solution, but with accelerated dissolution by strong alkaline solution derived from the electrochemical cell formation between sacrificial anode and cathodic core alloy. Corrosion products formed in the pit were effective for maintaining strong alkaline environment on the core alloy surface.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.