Al‐Mg‐Si合金の時効硬化現象に対するCuおよび(Cr+Fe)添加の影響
スポンサーリンク
概要
- 論文の詳細を見る
Age-hardening behavior of the Al–Mg–Si alloys added with (chromium + iron) and copper were investigated by hardness measurements and high-resolution transmission electron microscopy (HRTEM) . Age-hardenabilities of the alloys aged at 423 K increased with excess Si or Mg2Si contents. Cu addition increased their age-hardenability, whereas the addition of (Cr + Fe) decreased peak hardness. At the peak hardness in Cu-bearing alloys, the mean size of precipitates was smaller and the number density of precipitates was higher than those in Cu-free alloys. (Cr + Fe)-bearing alloys included AlSi(Cr, Fe) and AlSiFe dispersoids, which had depleted zones around them, and the number density of precipitates decreased in those alloys. Decrease in the number density of precipitates might be explained by consumption of solute atoms by the formation of dispersoids. It was confirmed that the Random-type precipitates existed in alloys aged at 423 K up to the peak hardness by HRTEM observation.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.