6061アルミニウム合金T651材の靭性値と破面変形量に及ぼす負荷速度の影響
スポンサーリンク
概要
- 論文の詳細を見る
It is believed that there exists a close relationship between the deformation on fracture surface and the fracture toughness. On the ductile fracture surface, it is known that macroscopic deformation called shear lip or plastic hinge is observed. In addition, microscopic deformation reflecting minute variation of geometry like fracture surface area is also associated with toughness. In this paper, measurement of fracture was performed by laser displacement meter and scanning laser microscope. Using these devices, instead of conventional planar measurement method, fracture surface can be measured stereoscopically. The macroscopic deformation, microscopic deformation, volume of shear lip and fracture surface area were determined, respectively. Therefore, it enables the investigation of the relationships between toughness at loading speed from 8.3 × 10−6 m/s to 8 m/s and these fracture surface features on 6061–T651 aluminum alloy. The results demonstrated that there is a good agreement between the variation of loading speed for toughness testing and the total fracture surface area.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.