過共晶Al‐Si合金の初晶Siの恒温晶出形態
スポンサーリンク
概要
- 論文の詳細を見る
In hyper-eutectic Al–Si alloys fabricated by 4–N aluminum and 5–N silicon, the morphology of primary silicon crystals at constant temperature of the solid-liquid co-existent temperature region was investigated. Supersaturated, non crystallization of silicon, alloy made by rapid solidification process were re-melted at the solid-liquid co-existent temperature region. The primary silicon was crystallized to the blocky shape. In the case of quenching by the solid-liquid temperature region after the melting, the primary silicon crystals grew to the petal shape. These crystallizations grew with same shape during isothermal holding at the solid-liquid co-existent temperature region. The primary silicon grew that the ration of length/width was reduced slightly, in the case of continuous cooling.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.