電子ビーム溶融法で銅を添加したAl‐Mg合金のCe‐Mo化成処理法による耐食性の改善
スポンサーリンク
概要
- 論文の詳細を見る
We investigated the corrosion resistance of Al–Mg(5052) alloys by means of the electro-chemical measurement, the immersion test and the observation of structures. The surface of alloys were modified by adding Cu with electronbeam melting method, and then coated with the oxide film contained Ge and Mo elements by three chemical treatments. The corrosion resistance of the alloy coated with the oxide film by immersing in the 4×10−3 kmol·m−3 Ce (CH3CO2)3 boiling aqueous solution for 5.4 ks was improved more than by the other chemical treatments. The small Ge and Mo were in the oxide film and the distribution of these element is not uniform. Especially the concentrations of Ge and Mo were high in the vicinity of the intermetallic compound (Al2Cu) . Micro voids and the other defects in the oxide films were increased with the increase in the intermetallic compound Al2Cu existing as secondary phase, and those defects affected as a corrosion initiation.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.