連続繊維強化TiAl合金へのSiC繊維の適合性
スポンサーリンク
概要
- 論文の詳細を見る
A SiCCVD fiber-reinforced TiAl matrix composites was fabricated by the sintering process. The compatibility of the strengthening fiber for the composites was investigated. The interfacial strength between the fiber and the matrix of the composites was improved by using the coated TiAl layer onto the SiCCVD fiber by the ion plating process. The interfacial shear strength was within the range of 160 MPa to 320 MPa. The coefficient of thermal expansion from 300 K to 1113 K was 11 × 10−6K−1 in the longitudinal direction, and was equivalent calculated values by the rule of mixture. The residual expansion was scarcely observed after the thermal cycling between 300 and 1113 K. However, the strength of extracted fiber from the composites was 3.1 GPa, decreased by 50% with the fiber strength of the as-received fiber.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.