Al‐Mg‐Si系合金のセレーションに及ぼす低温時効と復元処理の影響
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate effects of low temperature aging and reversion treatment on the serration of 6061 aluminum alloys, the reversion at from 423 to 853 K was conducted for the specimens in which the serration disappeared with the preliminary aging at 403 K. The measurements of electrical resistivity, DSC analysis and TEM micrographs showed that the solute atom concentration for the reversed specimens in which the serration generated again decreased remarkably due to formation of the precipitates, such as GP–zone, random-type, β″–phase, β′–phase and β–phase. Therefore, it was suggested that the disappearance of the serration was not affected by decrease of the solute atom concentration.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.