冷間圧接法による積層型5052アルミニウム合金/チタン複合材料の作製
スポンサーリンク
概要
- 論文の詳細を見る
5052 aluminum alloy matrix/titanium composites with about 8, 18 and 47 volume percents of titanium were fabricated by a simple method; compressing alternately multilayered 5052 aluminum alloy foils and pure titanium foils at room temperature. The initial thickness of titanium foils was 10, 25 or 102 μm and that of 5052 aluminum alloy foils was 115 μm. The composites obtained show the multilayered structure of the aluminum alloy and pure titanium phase extended in two dimensions. Many cracks are generated in titanium foils with the initial thickness of 10 μm during compressing and the number of cracks formed decreases with increasing thickness of titanium foils. No crack is detected in titanium foils with thickness of 102μm. Interlaminar shear strength between the aluminum alloy and titanium phases increases with the volume fraction of titanium phase and with the total reduction. The measured values of tensile strength of the composites are nearly in agreement with the values estimated from the rule of mixture on continuous-reinforced composites.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.