高純度アルミニウム中の鉛の表面偏析
スポンサーリンク
概要
- 論文の詳細を見る
Surface segregation of Pb in the annealed Al-foils has been studied by Rutherford back scattering spectroscopy (RBS) and transmission electron microscopy (TEM). High-purity Al-foils containing 100 mass-ppm Pb were heat-treated for 1 h or 4 h at 540°C. Almost all of Pb segregate in a thin layer, 0.1 μm from the surface. Lead contents in the Pb-enriched surface layers were estimated to be 0.1∼0.14 at% Pb which were about 100–fold higher than the initial bulk concentration. TEM observations show that Pb-particles are formed at foil surfaces and their size increases from about 80 nm to 240 nm when final annealing time increases from 1 h to 4 h at 540°C. The Pb particles have a cube-cube orientation relationship with Al matrix and are bounded by {100} and {111} facets.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.