高エネルギー遊星ボールミルによるAl95-xFexCr5混合粉末のメカニカルアロイング過程
スポンサーリンク
概要
- 論文の詳細を見る
Al95–xFexCr5 (X=10, 25, 35, 50) ternary powder mixtures and Al–(10, 25, 35, 50) at%Fe binary powder mixtures were mechanically alloyed by high-energy ball milling using a ball-to-powder weight ratio of 238: 10. The structural evolution during milling was investigated by X-ray diffraction techniques and transmission electron microscopy. The solid solutions of α–Al(Fe, Cr) and α–Fe(Cr) were formed in the early stage of milling for Al–Fe–Cr powder mixtures. In the case of Al–10 at%–5 at%Cr powder mixtures, the Al80Cr13.5Fe6.5 compound was formed and disappeared during milling, and Al5(Fe, Cr)2 and Al(Fe, Cr) were detected after longer time milling. In Al–25 at%–5 at%Cr powder mixtures, Al5(Fe, Cr)2, Al(Fe, Cr) and amorphous phases were consecutively formed during milling. In milling process of Al–35 at%–5 at%Cr and Al–50 at%–5 at%Cr powder mixtures, only the Al(Fe, Cr) compound was found and it finally became an amorphous phase. Retardation of amorphization was recognized in the Al–Fe–5 at%Cr ternary system, and the composition range of amorphous formation was almost in agreement with the results of enthalpy calculation for the solid solution and amorphous phase in the systems.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.