5083アルミニウム合金O材の極低温から高温における動的破壊靭性
スポンサーリンク
概要
- 論文の詳細を見る
Effect of temperature on mechanical properties of an 5083 aluminum alloy has been investigated for various testing temperatures from 10 to 773 K. For that purpose, the static tensile, dynamic fracture toughness test and fractography are carried out, and stop block method is employed to characterize fracture behavior at cryogenic temperatures. Mechanical properties such as 0.2% proof stress and ultimate tensile strength increase with decreasing temperature. The high temperature embrittlement, which has been often reported for 5000 series alloys having high Mg content, was not observed in the present study. The dynamic fracture toughness value, Jd, and dynamic crack extension toughness, Tmat, at 20 K are approximately 57% and 74% lower than that at 150 K, respectively. Fracture toughness at cryogenic temperatures shows strong dependence on formation of delamination cracks. The delamination cracks are initiated at grain boundaries. According to a SEM-EDX analysis, Mg is detected adjacent to the delamination cracks. Therefore, it is concluded that the formation of delamination cracks are concerned with β(Al3Mg2) phase at the grain boundaries.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.