異なる板厚形状を有する7475アルミニウム合金板材の超塑性ブロー成形
スポンサーリンク
概要
- 論文の詳細を見る
A new superplastic blow forming procedure for 7475 aluminum alloy sheets to provide the optimum distribution of thickness to a slender pan. The procedure adopts a preliminarily machined blank with different thickness locally before a superplastic forming (SPF). The figure and thickness for machining is calculated by a numerical analysis method developed for the pan to be formed with the optimum shape, size and thickness. This procedure also contains a friction between a sheet and a die, and work hardening of a blank material during SPF. It feeds the optimum pressurization schedule to the preliminarily machined blank to be formed with the maximum strain rate. A SPF of 7475 aluminum alloy sheets machined preliminarily to be formed a rectangular pan, in the ratio of the bottom to wall thickness is 2:1, according to the numerically calculated pressurizing schedule. The distribution of thickness in the formed pan was coincident with that of expected one.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.