アルミナ粒子分散Al‐Mg2Si合金複合材料における時効析出物の観察
スポンサーリンク
概要
- 論文の詳細を見る
Aging process of Al–1.0 mass% Mg2Si alloy composite materials with 4 vol% and 8 vol% Al2O3 particles was investigated by Vickers micro-hardness measurement and transmission electron microscope observation. When Al2O3 particles are dispersed into an Al–Mg–Si alloy, the age-hardenability was obviously lowered above at 473 K aging. The rectangular shaped spinels were observed at the interface between Al2O3 particles and the matrix. The overaged composite material with 4 vol% Al2O3 particles incluedes various kinds of metastable phase precipitates: namely β′ phase, the TYPE–B and TYPE–C precipitates of which crystal structures are different each other. Fraction of the three kinds of precipitates are the same as in the mother alloy containing 0.2 mass% excess Si. The composite material with 8 vol% Al2O3 particles contains the TYPE–A, TYPE–B and TYPE–C precipitates, but is free from β′ phase precipitates. The existence of those precipitates has correspondingly been observed in the mother alloy containing 0.4 mass% excess Si.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.