Al‐10%Mg合金の時効析出挙動および引張性質に及ぼす冷間加工の影響
スポンサーリンク
概要
- 論文の詳細を見る
An Al–10%Mg alloy was cold-rolled and aged in order to investigate the effects of cold working on the precipitation behavior and tensile properties. The specimens with various total reductions in area were isothermally aged at 413 K for up to 4.8 × 106 s. The precipitates were examined using optical microscopy, X-ray diffraction and differential scanning calorimetry. The precipitation was promoted by cold rolling and it was confirmed that the preferential precipitation of the stable precipitate, β-phase, at the shear bands was the reason for the stimulated precipitation. Full width of half maximum (FWHM) intensity of an X-ray diffraction peak, 0.2% proof stress and tensile strength showed peak values for the aging time of 1.8 × 106 s. Changes in 0.2% proof stress and tensile strength with aging time were affected by the precipitation and growth of a metastable precipitate, β'-phase, and the decrease in the concentration of solute Magnesium in the matrix.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.