An investigation on vacuum distillation of magnesium was carried out to obtain high purity material for basic research use, using a Mg–20%Al electrolytic magnesium (99.93%) base alloy as a raw material. Magnesium vapor was found to be condensed at a region where the temperature ranged from 625 K to 750 K involving steep temperature rise ascribed to the latent heat of condensation. To permit the condensation to occur uniformly on the sleeve, the temperature of the condenser portion was controlled within the above range. Purified magnesium of about 3 kg was obtained from the raw material of 4 kg by a distillation for 86.4 ks at 933 K. Impurities such as Fe, Mn, Si, commonly contained in commercial magnesium, were substantially eliminated by this distillation, resulting in a purity above 99.99% that was significantly increased from that (99.93%) of electrolytic magnesium.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.